Crack initiation in austenitic stainless steel sanicro 25 subjected to thermomechanical fatigue
 Petráš, Roman ; Škorík, Viktor ; Polák, Jaroslav
Thermomechanical fatigue experiments were performed with austenitic stainless Sanicro 25 steel. Several amplitudes of mechanical strain in a wide temperature interval (250-700 °C) were applied to the specimens. Mechanical response was recorded and fatigue lives were obtained. Scanning electron microscopy combined with FIB technique was used to study the mechanism of crack initiation in in-phase and in out-of-phase thermomechanical cycling. Different mechanisms of the crack initiation were found in these two types of loading. During in-phase loading fatigue cracks start in grain boundaries by cracking of the oxide. Cracks grew preferentially along grain boundaries which resulted in rapid crack initiation and low fatigue life. In out-of-phase loading multiple cracks perpendicular to the stress axis developed only after sufficiently thick oxide layer was formed and cracked in low temperature loading half-cycle. The cracks in oxide allowed localized repeated oxidation and finally also cracking. The cracks grow transgranularly and result in longer fatigue life.
Detailed record

Interested in being notified about new results for this query?
Subscribe to the RSS feed.
Digital Repository :: Search :: Submit :: Personalize :: Help
Powered by Invenio v1.1.2
Maintained by admin.invenio@techlib.cz
This site is also available in the following languages:
Česky  English